ASTALAC™ ABS MDA80
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 16oo7h_ASTALAC-ABS-MDA80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS MDA80 is a flame retardant, 7% fibre glass reinforced ABS injection moulding grade which meets the requirement of AS/NZS 60695.2.12 (IEC 60695-2-12) 960C glowwire flammability test. ASTALAC™ ABS MDA80 provides good balance of mouldability, superior flexual strength and rigidity and flame retardancy. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS MDA80UV ]. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 45.0 | MPa | ASTM D638 |
| Flexural Modulus 2(3.20 mm) | 4500 | MPa | ASTM D790 |
| Flexural Strength 3(3.20 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 4 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 230 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EPLAMID 66 FX0 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Hanwha Total TPE SE80 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |
| KEBAFLOW® LCP HF140 | BARLOG plastics GmbH | LCP | KEBAFLOW® |
| Sylvin 8378-85 Yellow 4202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Starflam POK 25V Z27 - BK84034 | Eurostar Engineering Plastics | PK-Aliphatic | Starflam |