LNP™ VERTON™ NV006E compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 15HeMV_LNP-VERTON-NV006E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON NV006E is a compound based on PC+ABS blend resin containing 30% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound PCA-F-7006 EM Product reorder name: NV006E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.52 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 132 | MPa | ASTM D638 |
| Yield | 150 | MPa | ISO 527-2 |
| Break | 130 | MPa | ASTM D638 |
| Break | 150 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.6 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2 |
| Break | 1.7 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8270 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 2 | 25 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 14.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 137 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-7022F | Spartech Polycom | PC | Spartech |
| DJSilicone NE-7170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Eltex® MED 100-MG12 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® MED |
| Karina WHITE PVC COMPOUND -E 854-10/185-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST ZK 8002NN01 | Ester Industries Ltd. | PC+ABS | ESTOPLAST ZK |