Bormed™ RE816CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 13wb9e_Bormed-RE816CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed RE816CF is a random copolymer This grade is suitable for the manufacturing of unoriented films on chill roll processes. CAS-No. 9010-79-1 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 800 | MPa | ISO 178 |
| Coefficient of Friction | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 450 | MPa | |
| TD : 50 µm | 450 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 35.0 | MPa | |
| TD : Yield, 50 µm | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 600 | % | |
| TD : Break, 50 µm | 600 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 145 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 120 | ASTM D2457 | |
| Haze (50.0 µm) | < 2.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 60G1 V30 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| NYLOY® NG-1112B | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Elastollan® 560 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| HAIPLEN EP50 TC4 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Lupoy® GN1006FMR | LG Chem Ltd. | PC | Lupoy® |