NORYL™ WCD795 resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 13EDnl_NORYL-WCD795-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as cable jacket of UL 62 SVE and NISPE configurations. Flame retardant performance capable of meeting UL 1581 VW-1 requirement. 90C or 105C temperature rating as defined by UL 62 TPE category. 79 Shore A hardness. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 11 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 23.0 | MPa | UL 1581 |
| Fracture 1 | 14.5 | MPa | ASTM D638 |
| Fracture, 136°C 2 | 21.5 | MPa | UL 1581 |
| Fracture | 14.5 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture | 310 | % | UL 1581 |
| Fracture 3 | 240 | % | ASTM D638 |
| Fracture, 136°C 4 | 250 | % | UL 1581 |
| Fracture | 220 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100mm span | 32.0 | MPa | ASTM D790 |
| -- | 30.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Heat Deformation (121°C) 6 | 8.0 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| VW-1 | Pass | UL 1581 | |
| Smoke Density | ASTM E662 | ||
| Flame, 0.5 mm plaque, Ds, max | 120 | ASTM E662 | |
| Non-Flame, 0.5 mm plaque, Ds, max | 70 | ASTM E662 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.4E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm, in Oil) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 24946D | Teknor Apex Company | TPV | Sarlink® TPV |
| Telcar® TL-2588L | Teknor Apex Company | TPE | Telcar® |
| Formolon® 616K | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |
| Karina GRAY COLOR CONCENTRATE 18/387-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PolyBlend™ 1100 80A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |