LNP™ THERMOCOMP™ RC008ESS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 12HyOy_LNP-THERMOCOMP-RC008ESS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RC008ESS is a compound based on PA66 resin containing Carbon Fiber. Added features include; Electrically Conductive, Easy Molding, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RC-1008 EM HS Product reorder name: RC008ESS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.80 | % | |
| Flow : 24 hr | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 254 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 24600 | MPa | ISO 178 |
| Flexural Stress | 375 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 70 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+2 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| KOCETAL® K700LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Hostacom TRC 377N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hostacom EP3307 C12463 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9993-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 505RU resin | SABIC Innovative Plastics | PC | LEXAN™ |