LG SAN 80HFICELLHK
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 121uKr_LG-SAN-80HFICELLHK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Transparency, Heat Resistance, Chemical Resistance Application Refrigerator Sleeves, Miscellaneous |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/10.0 kg | 29 | g/10 min | |
| 200°C/3.8 kg | 10 | g/10 min | |
| 200°C/5.0 kg | 3.0 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm, Injection Molded) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C, Injection Molded) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 3.20 mm, Injection Molded) | 3110 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C, 3.20 mm, Injection Molded) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.20 mm, Injection Molded) | 6.0 | % | ASTM D638 |
| Flexural Modulus 4(23°C, 3.20 mm, Injection Molded) | 3680 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 23°C, 3.20 mm, Injection Molded) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm, Injection Molded | 9.8 | J/m | |
| 23°C, 6.40 mm, Injection Molded | 9.8 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed, 6.40 mm Span) | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 6 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® PES TS0 | EPIC Polymers | PESU | TRIBOCOMP® |
| 3M™ Dyneon™ Fluoroelastomer FG 5630Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Galloo GP-rPS-86B | Galloo Plastics | PS (GPPS) | Galloo |
| Generic PEI - Glass Fiber, Milled | Generic | PEI | Generic |
| RTP 2200 HF Z | RTP Company | PEEK | RTP |