ULTEM™ AR9300 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 11vIeV_ULTEMAR9300resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 35 | kJ/m² | ISO 180/1U |
| 23°C | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 212 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 208 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ISO 306/A50 |
| -- | 210 | °C | ISO 306/B50 |
| -- | 215 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 1.7E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.29 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| OSU peak heat release rate 6 | 40.0 | kW/m² | FAR 25.853 |
| OSU total heat release 7 | 5.00 | kW·min/m² | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 350 - 370 | °C | |
| Middle Temperature | 350 - 400 | °C | |
| Front Temperature | 350 - 410 | °C | |
| Nozzle Temperature | 350 - 410 | °C | |
| Processing (Melt) Temp | 350 - 400 | °C | |
| Mold Temperature | 135 - 140 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| 6 . | 5 minute test |
| 7 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P40B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| SABIC® HDPE M453SE | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |
| Spartech Polycom EP5220 | Spartech Polycom | PP Homopolymer | Spartech |
| Keliren® XH-SJ | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Tunhe PET TH102C | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |