Durethan® BKV 30 FN00 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 10rylg_Durethan-BKV-30-FN00-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.43 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 23.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.62 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.18 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.22 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.080 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.1 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 9800 | 6000 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% Strain | -- | 128 | MPa | ISO 178/A |
| 23°C | 210 | 140 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 2.7 | 4.6 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 14-110, GF30; ISO 1043-PA GF FR (30+40+72) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | < 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 60 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | < 10 | -- | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 55 | 55 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 204 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 224 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.2E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.1E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength (23°C, 1.00 mm) | 37 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | V-0 | -- | ||
| 1.60 mm | V-0 5VA | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 800 | -- | °C | |
| Oxygen Index 9 | 32 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ POL050G10HI002L | ACLO Compounders Inc. | PC | ACCUTECH™ |
| EPT V Series™ PX-046 | Mitsui Chemicals, Inc. | EPDM | EPT V Series™ |
| HiPrene® MT42IN | GS Caltex | PP, Unspecified | HiPrene® |
| POLIMAXX 1102K | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Delon 3035 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |