RELENE® EE20
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 10rZgf_RELENE-EE20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EE20 is a High Density Polyethylene (HDPE) grade with low gel content, excellent elongation and orientation characteristics with negligible water carry-over. This grade is recommended for making low denier raffia tapes with very good elongation and moderate tenacity and recommended for wrapping fabrics for various applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 30.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 32.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 33.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 800 | % | |
| TD : Break, 40 µm, Blown Film | 850 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, Blown Film | 16 | g | |
| TD : 40 µm, Blown Film | 32 | g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287B | RTP Company | Nylon 610 | RTP |
| Shinko-Lac® ABS SE-3 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| FRIANYL® B3 GF30 V0 | Nilit Plastics | Nylon 6 | FRIANYL® |
| Karina GOLDY MB (SP31471) -E 45/ 28-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom EP3307 C12360 | LyondellBasell Industries | PP Copolymer | Hostacom |