EcoPaXX® Q-KGS6
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 10qFfg_EcoPaXX-Q-KGS6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-KGS6 is a Polyamide 410 (Nylon 410) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-KGS6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.8 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.6E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 6.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Biobased Content - Carbon | 60 | -- | % | ASTM D6866 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 255 to 265 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 285 | °C | |
| Processing (Melt) Temp | 265 to 295 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 G20 | NUREL, S.A. | Nylon 6 | Promyde® |
| RAYPRENE® NB221-S4086 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| TECHNYL STAR™ S 218 V35 BLACK 31 N | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Advanced Composites ATX-969 | Advanced Composites, Inc. | TPO | Advanced Composites |
| Elastron® V P.V101.A30.B | Elastron USA, Inc. | TPV | Elastron® V |