Grilamid® L 20A HL NZ nat
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 10V9gl_GrilamidL20AHLNZnat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid®L 20A HL NZ nat is a polyamide 12 (nylon 12) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Grilamid®The main features of L 20A HL NZ nat are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 0.980 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.6 | -- | % | ISO 294-4 |
| Flow | 1.0 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 1.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.60 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 65 | 65 | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1000 | 750 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 13 | 18 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 60 | 40 | kJ/m² | ISO 179/1eA |
| 23°C | 85 | 85 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature | ||||
| -- 1 | 90.0 - 100 | -- | °C | ISO 2578 |
| -- 2 | 150 | -- | °C | Internal method |
| Melting Temperature 3 | 179 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.7E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | 40 | 40 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.8 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA12-HI, GHL, 18-010 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ XLT65 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Torayca® 3101T-10V | Toray Resin Company | Nylon 66 | Torayca® |
| NANCAR® 3345 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| FHR Polypropylene P4G4Z-011 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Plaslube® POM CO GF20 TL15 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |