TECHNYL® A 50H1 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 100hsl_TECHNYL-A-50H1-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant polyamide 66, unreinforced, heat stabilised, for injection moulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.95 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.88 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3800 | 2200 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 86.0 | 53.0 | MPa | |
| Break | 75.0 | 46.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.2 | 22 | % | |
| Break | 21 | 140 | % | |
| Flexural Modulus | 3700 | 1710 | MPa | ISO 178 |
| Flexural Stress | 137 | 61.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.2 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 130 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 3.0 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 85.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | V-0 | -- | ||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature (1.60 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 BT TS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| SUPREME Specialty PS SP562 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Hostaform® S 27064 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| KOCETAL® LW301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LAPEROS® A150F | Polyplastics Co., Ltd. | LCP | LAPEROS® |