Ebalta AH 120 / GL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0zoIOA_Ebalta-AH-120-GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta 120/GL is a very low-viscous two-component epoxy resin with high strength values and fast curing. Due to its good soaking and wetting characteristics, this resin/hardener mixture is most suitable for solid parts with fabrics made of glass or carbon fibres. AH 120/GL is suitable as laminating resin for both large area- and thick laminates. Due to its almost odourless and skin-friendly GL hardener it is most suitable as laminating resin. With a mixing ratio of 100:40 you reach an about 15°C higher TG, slightly stiffer laminates as well as better impact resistance. The laminate thickness should not exceed 6-7 mm. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 to 86 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3000 to 3500 | MPa | ISO 178 |
| Flexural Stress | 100 to 120 | MPa | ISO 178 |
| Compressive Stress | 90.0 to 110 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 43 to 53 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 61.0 to 65.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 32 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.09 to 1.13 | g/cm³ | |
| Viscosity (25°C) | 0.83 to 1.0 | Pa·s | |
| Curing Time (20°C) | 12 to 16 | hr | |
| Pot Life 1(20°C) | 40 to 45 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8785-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polypropylene PPR Z9450 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| ADMER™ NE072E | Mitsui Chemicals Europe GmbH | PE, Unspecified | ADMER™ |
| EcoLon® GF1974-BK1 | Wellman Engineering Resins | Nylon 6 | EcoLon® |
| LUVOCOM® 80-7917 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |