AvaSpire® AV-848 CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0zXPls_AvaSpire-AV-848-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire® AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 CF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire® AV-848 CF30 can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 18800 | MPa | ASTM D638 |
| Tensile Strength 2 | 176 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 16500 | MPa | ASTM D790 |
| Flexural Strength | 259 | MPa | ASTM D790 |
| Compressive Strength | 145 | MPa | ASTM D695 |
| Shear Strength | 95.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 257 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | DSC |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| Thermal Conductivity | 0.037 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 382 - 404 | °C | |
| Mold Temperature | 166 - 193 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Back Pressure: Minimum |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ POL050G40L | ACLO Compounders Inc. | PC | ACCUTECH™ |
| Anjaflam® 100V-FR | Almaak International GmbH | PC | Anjaflam® |
| Generic TSU | Generic | TSU | Generic |
| Epocast 1619-A/B | Huntsman Advanced Materials | Epoxy | Epocast |
| HiFill® PA6/6 GF33 UV BK001 | Techmer Engineered Solutions | Nylon 66/6 | HiFill® |