GAPEX® RPP20EU05HB BLACK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0y2GXb_GAPEX-RPP20EU05HB-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®RPP20EU05HB BLACK is a polypropylene homopolymer (PP Homopoly) material, which contains a 20% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of RPP20EU05HB BLACK are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 3580 | MPa | ASTM D790 |
| Tangent : 23°C | 3720 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 0.565 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 141 | °C | ASTM D648 |
| Additional Information |
|---|
| Testing and measurements were performed at 73 +/-3°F and 50 +/-5% relative humidity unless otherwise noted. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2774N XRD1 | Teknor Apex Company | TPV | Sarlink® TPV |
| Zytel庐 HTN FR52G30BL BK337 | DuPont Performance Polymers | PPA | Zytel® HTN |
| CelloTherm™ T335 | Innovia Films Ltd. | CA | CelloTherm™ |
| INEOS PP 240xGB08 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| LNP™ STAT-KON™ Ultem_UC1200 compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |