TECHNYL® A 218 V25 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0wzDta_TECHNYL-A-218-V25-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNYL® A 218 V25 NATURAL is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America for injection molding. Important attributes of TECHNYL® A 218 V25 NATURAL are:
Typical application of TECHNYL® A 218 V25 NATURAL: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792, ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.85 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.700 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8400 | 6300 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 165 | 120 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 4.0 | -- | % | ASTM D638 |
| Break | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 7300 | -- | MPa | ASTM D790 |
| -- | 7300 | 5000 | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 57 | 87 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 80 | -- | J/m | ASTM D256 |
| 23°C | 8.5 | 15 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 245 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 85°C | 2.7E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 85°C | 2.7E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.380 mm | HB | -- | ||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTek KM6090 | KMI Group Inc. | PBT | PrimoTek |
| Moplen HP622J | LyondellBasell Industries | PP Homopolymer | Moplen |
| Durez® 32245 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Lucky Enpla LGF3300 | Lucky Enpla Co LTD | PBT | Lucky Enpla |
| SD POLYCA™ 875G10 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |