Epoxies, Ect. 10-3008
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxies, Etc. |
| Trademark: | Epoxies, Ect. |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0whhK2_Epoxies-Ect-10-3008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
10-3008 is a filled, high performance structural epoxy adhesive. 10-3008 is a flexible adhesive with outstanding lap shear and peel strength. It is a great choice for bonding substrates of differing coefficients of thermal expansion. 10-3008 is also an excellent adhesive for applications requiring impact and vibration resistance. 10-3008 has a convenient 1:1 by volume mix ratio and therefore is ideal for Dual Barrel Cartridge packaging. 10-3008 is stocked in 50ML and 200ML Dual Cartridge sizes. 10-3008 contains non-abrasive fillers and therefore is well suited for meter mix and dispense equipment. Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Peel Strength - T-Peel | |||
| 25°C 1 | 25.0 | piw | |
| 66°C 2 | 26.0 | piw | |
| 82°C 3 | 23.0 | piw | |
| 100°C 4 | 25.0 | piw | |
| 121°C 5 | 23.0 | piw |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 96000 | cP |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 6 | Beige | ||
| -- 7 | Grey | ||
| Mix Ratio by Weight (PBW) | |||
| Part A | 1.0 | ||
| Part B | 1.3 | ||
| Mix Ratio by Volume (PBV) | |||
| Part A | 1.0 | ||
| Part B | 1.0 | ||
| Density | |||
| 25°C 8 | 1.23 | g/cm³ | |
| 25°C 9 | 1.69 | g/cm³ | |
| Viscosity | |||
| 25°C 10 | 78 | Pa·s | |
| 25°C 11 | 650 | Pa·s | |
| Curing Time | |||
| 121°C | 0.50 | hr | |
| 82°C | 1.0 | hr | |
| 66°C | 2.0 | hr | |
| 25°C | 18 to 24 | hr | |
| Pot Life 12(25°C) | 60 | min | |
| Shelf Life | 12 | month |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 to 65 | ||
| Lap Shear Strength | |||
| -- 13 | 20.7 | MPa | |
| -- 14 | 20.7 | MPa | |
| -- 15 | 22.1 | MPa | |
| -- 16 | 18.6 | MPa | |
| -- 17 | 20.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 7 days |
| 2 . | 2 hours |
| 3 . | 1 hour |
| 4 . | 18 hours + 2 hours |
| 5 . | 30 minutes |
| 6 . | Part B |
| 7 . | Part A |
| 8 . | Part B |
| 9 . | Part A |
| 10 . | Part B |
| 11 . | Part A |
| 12 . | 100 grams |
| 13 . | AL/AL, 1 hours at 82.2°C |
| 14 . | AL/AL, 18 hours + 2 hours at 100°C |
| 15 . | AL/AL, 2 hours at 65.6°C |
| 16 . | AL/AL, 30 minutes at 121°C |
| 17 . | AL/AL, 7 days 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A700 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| E-RIALFILL H 15 20 T | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| Jam PE 60505 | Jam Petrochemical Company | HDPE | Jam PE |
| Lupolen 4021 K RM | LyondellBasell Industries | MDPE | Lupolen |
| Sylvin 8356-75 White 1555 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |