SABIC® LDPE 2201H0 is a grade without additives with a very good draw down ability. Films based on 2201H0 combine toughness with high tear strength and very good optical properties. Application Blown Film: SABIC® LDPE 2201H0 is typically used for thin packaging film purposes, where good optical properties are required. Cast Film: SABIC® LDPE 2201H0 can typically be used in a wide range of widths and thicknesses for e.g. lamination and bubble film. This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Features	Low density Optical Workability, good Good stripping Good tear strength Good toughness
Uses	Blown Film cast film
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	0.922	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.85	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	1.0		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested
-- ¹	25	µm
-- ²	50	µm
Tensile Modulus			ISO 527-3
MD : 25 µm, cast film	140	MPa	ISO 527-3
TD : 25 µm, cast film	140	MPa	ISO 527-3
MD : 50 µm, blown film	170	MPa	ISO 527-3
TD : 50 µm, blown film	170	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, cast film	9.00	MPa	ISO 527-3
TD : Yield, 25 µm, cast film	8.00	MPa	ISO 527-3
MD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
TD : Yield, 50 µm, blown film	11.0	MPa	ISO 527-3
MD : Fracture, 25 µm, cast film	24.0	MPa	ISO 527-3
TD : Fracture, 25 µm, cast film	17.0	MPa	ISO 527-3
MD : Broken, 50 µm, blown film	25.0	MPa	ISO 527-3
TD : Broken, 50 µm, blown film	20.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Fracture, 25 µm, cast film	260	%	ISO 527-3
TD : Fracture, 25 µm, cast film	580	%	ISO 527-3
MD : Broken, 50 µm, blown film	> 200	%	ISO 527-3
TD : Broken, 50 µm, blown film	> 500	%	ISO 527-3

Impact	Nominal Value	Unit	Test Method
Impact Strength			ASTM D4272
Blown Film : 50.0 µm	250	J/cm	ASTM D4272
Cast Film : 25.0 µm	220	J/cm	ASTM D4272

Additional Information	Nominal Value	Unit	Test Method
Blocking - Blown Film (50.0 µm)	50	g	Internal method
Re-blocking - Blown Film (50.0 µm)	100	g	Internal method
Tear Strength ³			ISO 6383-2
MD : 50.0 µm	55.0	kN/m	ISO 6383-2
TD : 50.0 µm	45.0	kN/m	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	96.0	°C	ISO 306/A

Optical	Nominal Value	Unit	Test Method
Gloss			ASTM D2457
45, 50.0 µm, blown film	68		ASTM D2457
45, 25.0 µm, cast film	73		ASTM D2457
Haze			ASTM D1003A
50.0 µm, blown film	6.0	%	ASTM D1003A
25.0 µm, cast film	3.6	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Cast FilmThe optical and film properties are determined on 25 µm cast film. Die gap 1.0 mm.Blown FilmFilm properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0vCxVg_SABIC-LDPE-2201H0.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Norpex® PPE AX190	Custom Resins Group	PPE	Norpex®
CP PRYME® Nylon 66 NN233HSL BK	Chase Plastics Services Inc.	Nylon 66	CP PRYME® Nylon 66
DAPCO™ 3050	Cytec Industries Inc.	Epoxy	DAPCO™
Geon™ Vinyl Flexible R5145B	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Kepital® F20-03BLW	KEP Americas	Acetal (POM) Copolymer	Kepital®