KumhoSunny PC/ASA HSC7079
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0vA6Rr_KumhoSunny-PC-ASA-HSC7079.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HSC7079 is a high heat resistance PC/ASA resin.PC/ASAHSC7079 has been widely used in Auto, such as rearview mirror . |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 | g/cm³ | ASTM D792 |
| -- | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.70 | % | ASTM D955 |
| -- | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 63.0 | MPa | ASTM D638 |
| -- | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- 1 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 70.0 | MPa | ASTM D790 |
| -- 2 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 52 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 3.20 mm | 600 | J/m | ASTM D256 |
| 23°C 5 | 46 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 129 | °C | ASTM D1525 6 |
| -- | 126 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 4J |
| 5 . | 5.5J |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LH01019 - C | Premier Polymers, LLC. | LLDPE | Premier |
| Telcar® TL-83F943D-OL BLU 729 | Teknor Apex Company | TPE | Telcar® |
| Texalan® 3 Series 365A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| Nanjing Hongrui PA6 B303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| Lumiloy® GP2100 | LG Chem Ltd. | PPE+PS | Lumiloy® |