SABIC® LLDPE 120W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0uv7TC_SABIC-LLDPE-120W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description 120W is a Linear Low Density Polyethylene grade featuring superior clarity for flexible packaging. Film exhibits excellent optical properties with good tensile and impact strength properties. Formulation: 1500 ppm Slip & 3000 ppm Antiblock Typical Applications High clarity applications, paper overwrap, produce and bread bags, garment and liners |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 30 µm | 260 | MPa | |
| TD : 30 µm | 270 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 10.0 | MPa | |
| TD : Yield, 30 µm | 9.00 | MPa | |
| MD : Break, 30 µm | 38.0 | MPa | |
| TD : Break, 30 µm | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 650 | % | |
| TD : Break, 30 µm | 810 | % | |
| Dart Drop Impact (30 µm) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 160 | g | |
| TD : 30 µm | 350 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 30.0 µm) | 90 | ASTM D2457 | |
| Haze (30.0 µm) | 10 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (30.0 µm) | 600 | J/cm | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 to 215 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 2806 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Malen E FGNX 23-D006 | LyondellBasell Industries | LDPE | Malen |
| LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Lupoy® GP1006FL | LG Chem Ltd. | PC | Lupoy® |
| Lushan PF-300 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |