RTP EMI 960.5
| Category: | PSU , Polysulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0trXSg_RTP-EMI-960-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Moisture Content | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 5.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+6 | ohms | ASTM D257 |
| -- | < 1.0E+5 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 332 - 357 | °C | |
| Mold Temperature | 93.3 - 149 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 50GF | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Starflam RF0077P | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| Verolloy B2505LD | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Geon™ Specialty Suspension Atlas S140 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ Specialty Suspension |
| Hostacom BB 73 F | LyondellBasell Industries | PP Copolymer | Hostacom |