XAREC™ EA 537
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0tg8St_XAREC-EA-537.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Crystalline Polymers - 30% Glass Filled, Ignition Resistant, Impact Modified Polymer for Electronic and Electrical Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 2.00mm | 0.30 - 0.70 | % | Internal method |
| Flow direction : 2.00mm | 0.10 - 0.30 | % | Internal method |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10900 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 32 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed 2 | 265 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed 3 | 240 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed 4 | 225 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | TMA | ||
| Flow : -30 to 30°C | 1.5E-5 | cm/cm/°C | TMA |
| Lateral : -30 to 30°C | 4.7E-5 | cm/cm/°C | TMA |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.20 | IEC 60250 | |
| Dissipation Factor | 2.0E-3 | IEC 60250 | |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 2 | IEC 60112 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C |
| Injection instructions |
|---|
| Mold Temperature for optimal gloss and heat resistance: 130 to 155°C |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | 150°C tool |
| 3 . | 150°C tool |
| 4 . | 80°C tool |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP23-566-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Zytel® E51HSB NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| ELASTOSIL® R 570/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Perlast® G76W | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| Polyrocks 8200EP75V | Polyrocks Chemical Co., Ltd | TPE | Polyrocks |