Nyloi A2 GF/30 TF NATURALE
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nyloi |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0tT0gO_Nyloi-A2-GF-30-TF-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nyloi A2 GF/30 TF NATURALE is a Polyamide 66 (Nylon 66) material. It is available in Europe, Latin America, or North America for injection molding. Important attributes of Nyloi A2 GF/30 TF NATURALE are:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.45 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 6.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 170 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.61 | ||
| vs. Steel - Static | 0.41 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostaform® LX90Z | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| LUVOCOM® 1100-8134 | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| Sylvin 7833-70C Red 6199 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dryflex® SE 35A201 | ELASTO | TPE | Dryflex® |