Tarnamid® T-27 MK30

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Grupa Azoty S.A.
Trademark:	Tarnamid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0sBgaf_Tarnamid-T-27-MK30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Tarnamid® T-27 MK30 is a Polyamide 6 (Nylon 6) material filled with 30% mineral. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding.

Important attributes of Tarnamid® T-27 MK30 are:

Chemical Resistant

Fatigue Resistant

Flame Retardant

Food Contact Acceptable

Good Aesthetics

Typical applications include:

Automotive

Engineering/Industrial Parts

Construction Applications

Electrical/Electronic Applications

Fabrics/Fibers

General Information
Filler / Reinforcement	Mineral, 30% Filler by Weight
Features	Acid Resistant Base Resistant Fatigue Resistant Flame Retardant Food Contact Acceptable Good Abrasion Resistance Good Chemical Resistance Good Dimensional Stability Good Strength High Hardness High Heat Resistance High Impact Resistance High Stiffness Low Friction Medium Rigidity Opticals Solvent Resistant Vibration Damping
Uses	Automotive Electronics Automotive Exterior Parts Automotive Interior Parts Automotive Under the Hood Connectors Food Packaging Furniture Household Goods Machine/Mechanical Parts Monofilaments Profiles Reinforced Panels Rods Safety Helmets Sporting Goods Tubing
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.35	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (275°C/5.0 kg)	60	g/10 min	ISO 1133
Water Absorption (23°C, 24 hr)	1.0	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)	200	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4500	MPa	ISO 527-2
Tensile Stress (Yield)	75.0	MPa	ISO 527-2
Tensile Strain (Break)	6.0	%	ISO 527-2
Flexural Modulus	4000	MPa	ISO 178
Flexural Stress (3.5% Strain)	110	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	45	kJ/m²	ISO 179/1eU
Notched Izod Impact Strength	5.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	65.0	°C	ISO 75-2/A
Vicat Softening Temperature	200	°C	ISO 306/B50

Injection	Nominal Value	Unit
Drying Temperature	80.0 to 100	°C
Drying Time	2.0 to 4.0	hr
Suggested Max Moisture	0.20	%
Processing (Melt) Temp	250 to 290	°C
Mold Temperature	80.0 to 120	°C
Injection Pressure	80.0 to 130	MPa
Injection Rate	Moderate

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3714	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Kaneka MUH K-7	Kaneka Corporation	ABS	Kaneka MUH
LNP™ LUBRICOMP™ JFL34 compound	SABIC Innovative Plastics	PESU	LNP™ LUBRICOMP™
POLYCASA® ACRYL KR 2008/1	Polycasa	Acrylic (PMMA)	POLYCASA® ACRYL
Starex VH-0815 M	LOTTE ADVANCED MATERIALS CO., LTD.	ABS	Starex