| Higher gloss, wider processing window version of Geon HTX Ultra LA426G. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 441311640000 | ASTM D4216 | |
| PVC Cell Classification | 14215 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1920 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 36.0 | MPa | ASTM D638 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Flexural Strength | 58.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 490 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 52.0 | J/cm | ASTM D4226 |
| 23°C 4 | 111 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 88.3 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 87.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 81.1 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 85.0 | °C | ASTM D648 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm, BK | HB | UL 94 | |
| 3.0 mm, BK | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit.Physical properties measured on LA436G Black 2880. This version produces the highest gloss, higher impact and can be run at lower extruder temperatures than standard LA426G product. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Program A, C.125 Dart |
| 4 . | Program B, C.125 Dart |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HO-20GF | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| TRISTAR® PC-10R-(18) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Arak HDPE I1 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| FERREX® GPP35CF56UL BLACK | Ferro Corporation | PP Homopolymer | FERREX® |
| Karina IVORY PVC COMPOUND 70921-35/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |