SURPASS® FPs117 Series
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ratc9_SURPASS-FPs117-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FPs117-C (PPA): Lamination film, coextruded sealant layer, and high toughness film FPs117-D (1000 ppm Slip, 2500 ppm AB, PPA): Lamination film, coextruded sealant layer, and high toughness film |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 126 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 132 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| MD : Break, 25 µm, Blown Film | 46.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 42.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 540 | % | |
| TD : Break, 25 µm, Blown Film | 760 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 400 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 300 | g | |
| TD : 25 µm, Blown Film | 450 | g | |
| Seal Initiation Temperature (25 µm, Blown Film) | 100 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.0 µm, Blown Film 1 | 72 | ||
| 45°, 25.0 µm, Blown Film 2 | 37 | ||
| Haze | ASTM D1003 | ||
| 25.0 µm, Blown Film 3 | 7.0 | % | |
| 25.0 µm, Blown Film 4 | 16 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (25.0 µm) | 790 | J/cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | LDPE Blended |
| 2 . | 100% LLDPE |
| 3 . | LDPE Blended |
| 4 . | 100% LLDPE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA6 2004/39 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| KPOL-HDPE HD K-20/960 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| KOCETAL® WR301LODG | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Huaxia Shenzhou DS601 | Shandong Huaxia Shenzhou New Material Co., Ltd. | FEP | Huaxia Shenzhou |
| Infino CF-1070 | SAMSUNG SDI CO., LTD. | PC | Infino |