Amodel AS- 4133 HS is a 33% glass fiber reinforced, lubricated and thermally stable polyphthalamide (PPA ), which can be quickly processed and molded in water temperature molds. Conventional applications include electrical and electronic components, especially electronic and electrical components for automotive systems. -Black: AS-4133 HS BK 324 natural color: AS-4133 HS NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	heat stabilizer Lubricant demoulding
Features	Good dimensional stability Low hygroscopicity Rigid, good High strength Laser welding Fast molding cycle Good creep resistance Good chemical resistance Heat resistance, high Hot water formability Thermal Stability Lubrication
Uses	Lawn and Garden Equipment Electrical/Electronic Applications Valve/valve components Industrial components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field Mobile phone General
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.45	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.50	--	%	ASTM D955
Transverse flow	1.0	--	%	ASTM D955
Water Absorption (24 hr)	0.29	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	11700	11700	MPa	ASTM D638
23°C	12600	--	MPa	ISO 527-2
100°C	6830	--	MPa	ISO 527-2
150°C	5310	--	MPa	ISO 527-2
175°C	4830	--	MPa	ISO 527-2
Tensile Stress
Fracture, 23°C	211	--	MPa	ISO 527-2
Fracture, 100°C	125	--	MPa	ISO 527-2
Fracture, 150°C	87.6	--	MPa	ISO 527-2
Fracture, 175°C	79.3	--	MPa	ISO 527-2
--	200	172	MPa	ASTM D638
Tensile Elongation
Fracture	2.5	2.2	%	ASTM D638
Fracture, 23°C	2.6	--	%	ISO 527-2
Fracture, 100°C	4.3	--	%	ISO 527-2
Fracture, 150°C	6.6	--	%	ISO 527-2
Fracture, 175°C	6.6	--	%	ISO 527-2
Flexural Modulus
--	11000	11000	MPa	ASTM D790
23°C	10400	--	MPa	ISO 178
100°C	7170	--	MPa	ISO 178
150°C	4620	--	MPa	ISO 178
175°C	4210	--	MPa	ISO 178
Flexural Strength
--	290	241	MPa	ASTM D790
23°C	296	--	MPa	ISO 178
100°C	177	--	MPa	ISO 178
150°C	111	--	MPa	ISO 178
175°C	99.3	--	MPa	ISO 178
Compressive Strength	179	172	MPa	ASTM D695
Shear Strength	89.6	75.8	MPa	ASTM D732
Poisson's Ratio	0.41	--		ASTM E132

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	67	--	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	80	69	J/m	ASTM D256
23°C	9.7	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact
--	960	--	J/m	ASTM D256
23°C	59	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, annealed, 3.20mm	320	--	°C	ASTM D648
1.8 MPa, not annealed	294	--	°C	ISO 75-2/A
1.8 MPa, annealed, 3.20mm	300	--	°C	ASTM D648
Continuous Use Temperature ¹	210	--	°C	ASTM D3045
Melting Temperature	327	--	°C	ASTM D570, ISO 11357-3
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	2.0E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	1.5E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	7.6E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	1.2E-4	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	2.0E+16	5.0E+14	ohms·cm	ASTM D257
Dielectric Strength (1.60 mm)	20	20	kV/mm	ASTM D149
Dielectric Constant				ASTM D150
60 Hz	3.80	4.30		ASTM D150
1 MHz	3.60	3.40		ASTM D150
Dissipation Factor				ASTM D150
60 Hz	4.0E-3	0.020		ASTM D150
1 MHz	0.012	0.019		ASTM D150
Comparative Tracking Index (CTI)	600	600	V	UL 746
High Voltage Arc Tracking Rate (HVTR)	14.0	18.0	mm/min	UL 746

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating ²(3.20 mm)	HB	--		UL 94

Optical	Dry	Conditioned	Unit	Test Method
Transmittance ³				ASTM D1003
1070 nm : 1.60 mm	> 20	--	%	ASTM D1003
940 nm : 1.60 mm	> 20	--	%	ASTM D1003

Injection instructions
射出速度： 3〜4英寸/秒保压压力：射出压力的50%

Note Message
1 .	1500 hours
2 .	These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations.
3 .	Light transmittance, natural color grade

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0rCNMo_Amodel-AS-4133-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3980H	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Ravago Compounds HM-307M (Comp)	Ravago Manufacturing Americas, LLC	LLDPE	Ravago Compounds
Thermylene® P7-40FG-0600	Asahi Kasei Plastics North America Inc.	PP, Unspecified	Thermylene®
Electrafil® PS-31/EC	Techmer Engineered Solutions	PS (GPPS)	Electrafil®
Lucofin® 7440 HFFR	Lucobit AG	Polyolefin, Unspecified	Lucofin®