TARFLON™ LC1402
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0phHAx_TARFLONLC1402.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Light guiding, High flow, Good color tone |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 125 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 2.00mm | 0.50 - 0.70 | % | Internal method |
| Flow : 2.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.23 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 120 | °C | ISO 75-2/A |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.40 mm, NC) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | |
| Transmittance | 90.0 | % | ISO 13468-1 |
| Haze (3000 µm) | 0.50 | % | ASTM D1003 |
| Yellowness Index 2 | 0.95 | YI |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 - 8.0 | hr | |
| Rear Temperature | 280 - 350 | °C | |
| Middle Temperature | 280 - 350 | °C | |
| Front Temperature | 280 - 350 | °C | |
| Mold Temperature | 80 - 110 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | D65 type, 10° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BMN Y TLD | Arkema | Nylon 11 | Rilsan® |
| RTP ESD A 203 | RTP Company | Nylon 66 | RTP |
| Mirathane™ E195F | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Nypol® PA A3 ST HS UV5 PRTA011 NR427 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Adell Polyamide AW-38 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |