KIBISAN® PN-106 L150 FG
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBISAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0pXCtq_KIBISANPN106L150FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Food Contact SAN KIBISAN PN-106 L150 FG Product Description: High clarity |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.20 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Flexural Stress 2 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, not annealed | 88.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/A50 |
| -- | 101 | °C | ISO 306/B50 |
| CLTE - Flow | 3.6E-5 - 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® EME-6310H | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Karina IVORY PVC COMPOUND 851-35/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ KAL22M compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| PLUSTEK RA502 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Ingeo™ 6260D | NatureWorks® LLC | PLA | Ingeo™ |