CYCOLOY™ CY6414 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0p33PC_CYCOLOY-CY6414-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame retardant modified PC blend using non-brominated and non-chlorinated flame retardant systems, offering high heat for application in appliances, lighting and electrical market. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2330 | MPa | ASTM D638 |
| -- | 2430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 66.4 | MPa | ISO 527-2/50 |
| Break 3 | 62.0 | MPa | ASTM D638 |
| Break | 67.9 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 5.7 | % | ISO 527-2/50 |
| Break 5 | 85 | % | ASTM D638 |
| Break | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 6 | 2470 | MPa | ISO 178 |
| Flexural Stress | 96.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 12 12 | kJ/m² | |
| 23°C | 20 20 | kJ/m² | |
| Charpy Unnotched Impact Strength 8 | ISO 179/1eU | ||
| -30°C | No Break No Break | ||
| 23°C | No Break No Break | ||
| Notched Izod Impact Strength 9 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact Strength 10 | ISO 180/1U | ||
| -30°C | No Break No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 118 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 116 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/B50 |
| -- | 135 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C 12 | Pass | ||
| 125°C | Pass | ||
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 95.0 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.01 | ||
| 1 MHz | 2.95 | ||
| Dissipation Factor | |||
| 1 kHz | 1.7E-3 | ASTM D150 | |
| 1 MHz | 8.8E-3 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | V-0 | ||
| 2.50 mm | 5VB | ||
| Glow Wire Flammability Index 13(0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 14 | IEC 60695-2-13 | ||
| 0.750 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| 3.00 mm | 775 | °C | |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 210 to 260 | °C | |
| Middle Temperature | 230 to 290 | °C | |
| Front Temperature | 240 to 300 | °C | |
| Nozzle Temperature | 230 to 290 | °C | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | by VDE |
| 13 . | by VDE |
| 14 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 4404N-PE | TSRC Corporation | TPE | T-Blend® |
| APEX® 3311-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| LONGLITE® PBT 3015-104X | CCP Group | PBT | LONGLITE® PBT |
| Plexiglas® Diffuse V045-68192 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| apilon 52® TL 45 NS | API SpA | TPU-Polyether | apilon 52® |