Order Products : sales@su-jiao.com
PRL PC-FR2-TFE
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0oQNd0_PRL-PC-FR2-TFE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-FR2-TFE is a Polycarbonate (PC) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 to 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 56.9 | MPa | |
| Break, 3.18 mm | 56.9 | MPa | |
| Tensile Elongation (Yield, 3.18 mm) | > 10 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 135 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 129 | °C | |
| RTI Elec | UL 746 | ||
| 1.60 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.60 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Str | UL 746 | ||
| 1.60 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 76.7 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 GB 10 | RTP Company | PBT | RTP |
| Surlyn® 8320 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| TRIBOCOMP® PA612 CF30 TS0 | EPIC Polymers | Nylon 612 | TRIBOCOMP® |
| Xuchuan XCS-2009S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Sylvin 5153-89 Blue 8323 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |