Celstran® PA66-GF30-02
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0nhAdM_Celstran-PA66-GF30-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% long glass fiber reinforced, heat stabilized, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 9310 | MPa | ASTM D638 |
| 23°C | 10300 | MPa | ASTM D638 |
| 121°C | 5310 | MPa | ASTM D638 |
| -- | 9700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 228 | MPa | ASTM D638 |
| Fracture, 23°C | 194 | MPa | ASTM D638 |
| Fracture, 121°C | 110 | MPa | ASTM D638 |
| Fracture | 170 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.5 | % | ASTM D638 |
| Fracture, 23°C | 2.4 | % | ASTM D638 |
| Fracture, 121°C | 2.7 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 252 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 315 | °C | |
| Processing (Melt) Temp | 300 - 315 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 315°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AQUATUF® HMP-335 (Roto) | Ravago Manufacturing Americas, LLC | HDPE | AQUATUF® |
| ELIX™ ABS E211 LNS013 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Halene L 71501S | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| Hylon® N1000EHL2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Durethan® BKV 50 H2.0 EF DUS030 901510 | LANXESS Corporation | Nylon 6 | Durethan® |