WELLAMID Nylon 6600/58 GV 30 HWUVCP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0nFGeo_WELLAMIDNylon660058GV30HWUVCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6600/58 GV 30 HWUVCP is a polyamide 66 (nylon 66) material, which contains a 30% glass fiber reinforced material. This product is available in Europe,. The main features of WELLAMID Nylon 6600/58 GV 30 HWUVCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Transverse flow : 4.00mm | 0.70 | -- | % | |
| Flow : 4.00mm | 0.20 | -- | % | |
| Water Absorption (Saturation, 23°C) | 1.8 - 2.3 | -- | % | DIN 53495 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7500 | 5000 | MPa | ISO 527-2 |
| Tensile Stress | 135 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.6 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | 6500 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | 36 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 70 | -- | kJ/m² | ISO 179 |
| 23°C | 85 | 110 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 230 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | -- | °C | ISO 306/B50 |
| Melting Temperature | 255 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 2.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 40 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.15 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | HB | UL 94 | |
| 3.2 mm | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 265 - 290 | °C | |
| Mold Temperature | 70 - 100 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 CF20 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| THORNEL® P-55 | Cytec Industries Inc. | Carbon/Epoxy | THORNEL® |
| Cri-Line LC-512-55-BR | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Hy-Vin® XQ76054 | INEOS Compounds | PVC, Rigid | Hy-Vin® |
| LEXAN™ 123X resin | SABIC Innovative Plastics | PC | LEXAN™ |