Edgetek™ TR2-10GF/000 NATURAL
| Category: | Copolyester , Copolyester |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0mE5qA_Edgetek-TR2-10GF-000-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Eastman Tritan™ copolyester these compounds provide chemical resistance, clarity, heat resistance and BPA-free solutions. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2760 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 60.0 | MPa | |
| Break 3 | 53.1 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield 4 | 5.0 | % | |
| Break 5 | 13 | % | |
| Flexural Modulus 6 | 2760 | MPa | ASTM D790 |
| Flexural Strength 7 | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C, 3.18 mm, Injection Molded) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 108 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -30 to 30°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 266 to 282 | °C | |
| Mold Temperature | 60.0 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 5.1 mm/min |
| 5 . | Type I, 5.1 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| CALIBRE™ 303V-10 | Trinseo | PC | CALIBRE™ |
| KumhoSunny PC/ABS HAC8250TC | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina IVORY PVC COMOUND -E 704-35/ 1-J-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Optix® CA-42 | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |