Ultramid® A3XG3 BK20562
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0lY4IU_Ultramid-A3XG3-BK20562.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3XG3 BK20562 is a 15% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term heat stability. The grade is based on red phosphorous and exhibits exceptional mechanical properties and outstanding surface finish. Flame performance has been determined to be V0 at 0.8mm per the UL94 method. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.50 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6740 | 4450 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | 5.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6150 | 4090 | MPa | ISO 178 |
| Flexural Stress (23°C) | 183 | 125 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 4.2 | 4.0 | kJ/m² | |
| 23°C | 4.8 | 5.6 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 35 | 23 | kJ/m² | |
| 23°C | 45 | 49 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 4.5 | 3.8 | kJ/m² | |
| 23°C | 4.8 | 5.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 222 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 4571 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| SABIC® LDPE PCG07 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Chemical Resources HD5953 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| LNP™ THERMOCOMP™ 9X07430 compound | SABIC Innovative Plastics | PC+PBT | LNP™ THERMOCOMP™ |
| OmniTech™ HDPE TF10 | OMNI Plastics, LLC | HDPE | OmniTech™ |