Glass-fibre reinforced epoxy moulding compound Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures Primary application(s): Connectors, Thermocouples, Sensors, Resistors, Potentiometers This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 to 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.85 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Post Shrinkage 1 | < 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 to 18000 | MPa | ISO 527-2 |
| Tensile Stress | 60.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus | 14000 to 16000 | MPa | ISO 178 |
| Flexural Stress | 120 to 140 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.5 to 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 8.0 to 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 170 to 190 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.5E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.60 to 0.80 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 to 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 25 to 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 7.00 5.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.030 | ||
| 1 MHz | 0.010 to 0.030 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (5.70 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 900 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B300MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Unichem 7011C2-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Haysite SMC 43000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| Karina YELLOW PVC COMPOUND 602D02/101-C-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DL004 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |