RTP VLF 84007
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0iGHT6_RTP-VLF-84007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long Glass Fiber - Heat Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15200 | MPa | ASTM D638 |
| Tensile Strength | 228 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.5 - 2.5 | % | ASTM D638 |
| Flexural Modulus | 14500 | MPa | ASTM D790 |
| Flexural Strength | 324 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 290 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 820 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 277 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 304 - 329 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VE800 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| Shandong PA610 A6MG9301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| VisiJet® SL Tough | 3D Systems | Epoxy | VisiJet® |
| NITRIFLEX PDC-7421 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Boda BDF-H2902 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |