Generic PS (IRPS)
| Category: | PS (IRPS) , Ignition Resistant Polystyrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0hvS4m_Generic-PS-IRPS-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PS (IRPS) This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 - 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.4 - 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 13.8 - 29.0 | MPa | ASTM D638 |
| Fracture, 23°C | 10.3 - 24.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 - 41 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1800 - 2300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 98 - 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 77.7 - 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.9 - 100 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 215 - 250 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PS (IRPS)This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® PH030E04 | POLYMAT | PP Homopolymer | Prixene® |
| RTP EMI 2861-60A | RTP Company | TPO (POE) | RTP |
| TAIRIPRO T1002 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| TULAMID® PA-SV30 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Xuchuan A-7001/B-8001D | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |