Infino GC-1022
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0gvwXP_InfinoGC1022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino GC-1022 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 19 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 56.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 95 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 78.0 | MPa | ASTM D790 |
| -- 8 | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 64 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 740 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 610 | J/m | ASTM D256 |
| 23°C 10 | 58 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 4342L | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Nanjing Hongrui PC CT306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| BCC Resins BC 5200 | BCC Products Inc. | Epoxy | BCC Resins |
| Alathon® L5440 | LyondellBasell Industries | HDPE | Alathon® |
| Borealis PP BJ100HP | Borealis AG | PP Copolymer | Borealis PP |