BJB Polyurethane F-82 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0gn6ky_BJB-Polyurethane-F-82-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The F-82 A/B system is a production oriented, non-mercury containing, fast gel, and fast de-mold material. It features a working time which allows time to mix, vacuum de-gas, and pour air-free parts. F-82 A/B can be demolded in as little as two hours depending on part size and configuration. PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.04 | g/cm³ | |
| -- | 1.09 | g/cm³ | ASTM D792 |
| -- 2 | 1.14 | g/cm³ | |
| Specific Volume | 0.936 | cm³/g | |
| Shrinkage | 0.70 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 5.5 | min | |
| Work Time 3(25°C) | 4.5 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 75 - 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2.51 | MPa | ASTM D412 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 14.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 390 | % | ASTM D412 |
| Tear Strength | 31.2 | kN/m | ASTM D624 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 4.59 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.064 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 50, mixing ratio by capacity: 46 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 4 | 1500 | cP | Brookfield |
| 25°C 5 | 850 | cP | Brookfield |
| 25°C | 1300 | cP | Brookfield |
| Demold Time (25°C) | 120 - 180 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Physical properties obtained from test specimens post cured per recommended procedure.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 130-160°F (54-71°C). |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Part B |
| 5 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F37-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Silplus® 50 MP | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Zhongfa PP ZF-T40 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Daelim Po1y® LH-6070UV | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| RTP 2299 X 126107 A | RTP Company | PEEK | RTP |