NOVAPOL® LF-0422-F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ggY9E_NOVAPOLLF0422F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL®LF-0422-F is a low density polyethylene material,. This product is available in North America and is processed by co-extrusion or cast film. NOVAPOL®The main features of the LF-0422-F are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Cast Film) | 0.26 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% sectioning, MD : 38 µm, cast film | 142 | MPa | ASTM D882 |
| 1% sectioning, TD : 38 µm, cast film | 171 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : yield, 38 µm, extruded film | 10.3 | MPa | ASTM D882 |
| TD : yield, 38 µm, extruded film | 9.40 | MPa | ASTM D882 |
| MD : Fracture, 38 µm, extruded film | 18.9 | MPa | ASTM D882 |
| TD : Fracture, 38 µm, extruded film | 11.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm, extruded film | 290 | % | ASTM D882 |
| TD : Fracture, 38 µm, extruded film | 530 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, cast film | 320 | g | ASTM D1922 |
| TD : 38 µm, cast film | 320 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 38.0 µm, cast film) | 89 | ASTM D2457 | |
| Haze (38.0 µm, cast film) | 2.6 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 + PA66/6 A 2030/100 GF30 | ALBIS PLASTIC GmbH | Nylon 6+Nylon 66/6 | ALTECH® PA6 + PA66/6 |
| Keyflex® BT 1047D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Luran® S Q440 | Styrolution | ASA | Luran® S |
| Paxon™ BA50-100 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| SQUARE® LIM3600-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |