Axiall PVC HHP-190 Datasheet,PVC, Rigid,Axiall Corporation-SHANGHAI SUSHENG

Message
Georgia Gulf HHP-190 is a special purpose profile extrusion alloy designed for application requiring the following properties: Heat Resistance & Thermal Stability Impact Strength and toughness Colorability UV Color Stability Dimensional Stability Chemical Resistance.

General Information
Features	Good dimensional stability Impact resistance, good Good color stability Good coloring Good chemical resistance Heat resistance, medium Thermal stability, good Good toughness
Forms	Particle
Processing Method	Profile extrusion molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.27	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	110		ASTM D785
Durometer Hardness (Shore D)	80		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2410	MPa	ASTM D638
Tensile Strength (Yield)	46.2	MPa	ASTM D638
Flexural Modulus	2410	MPa	ASTM D790
Flexural Strength	76.5	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	530	J/m	ASTM D256
Tensile Impact Strength	96.7	kJ/m²	ASTM D1822
Drop Impact Resistance	133	J/cm	ASTM D4226

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	96.1	°C	ASTM D648
1.8 MPa, not annealed	87.8	°C	ASTM D648
CLTE - Flow	7.4E-5	cm/cm/°C	ASTM D696

Extrusion	Nominal Value	Unit
Drying Temperature	76.7	°C
Drying Time	2.0 - 6.0	hr
Cylinder Zone 1 Temp.	149	°C
Cylinder Zone 2 Temp.	154	°C
Cylinder Zone 3 Temp.	160	°C
Cylinder Zone 4 Temp.	166	°C
Cylinder Zone 5 Temp.	171	°C
Melt Temperature	188 - 199	°C
Die Temperature	177	°C

Extrusion instructions
Georgia Gulf HHP-190 is mildly hygroscopic. Drying before extrusion is recommended at 170°F for 2 to 6 hours to ensure optimum performance and surface characteristics.Recommended Extruder Size and Screw Design:For Screw L/D of 60"/2.5" Extr. L/D: 24:1 # Feed Flights: 5 Feed Depth: 0.500 to 0.575 in # Metering Flights: 5 to 12 Metering Depth: 0.200 to 0.210 in Comp. Ratio: 2.0 to 2.5 For Screw L/D of 84"/3.5" Extr. L/D: 24:1 # Feed Flights: 5 Feed Depth: 0.600 to 0.700 in # Metering Flights: 5 to 12 Metering Depth: 0.240 to 0.280 in Comp. Ratio: 2.0 to 2.5 Other Barrel Temperatures:Gate Temperature: 350°FAfter start-up, temperature adjustments up or down may be necessary until extrusion impact, surface, and die flow are acceptable. Adjustments in 5°F increments are recommended. Normally Zone 1 temperature should not be varied since feed rate may be affected.If a screen pack is used, a 20/40 mesh combination should be sufficient.

Extrusion instructions

Georgia Gulf HHP-190 is mildly hygroscopic. Drying before extrusion is recommended at 170°F for 2 to 6 hours to ensure optimum performance and surface characteristics.Recommended Extruder Size and Screw Design:For Screw L/D of 60"/2.5" Extr. L/D: 24:1 # Feed Flights: 5 Feed Depth: 0.500 to 0.575 in # Metering Flights: 5 to 12 Metering Depth: 0.200 to 0.210 in Comp. Ratio: 2.0 to 2.5 For Screw L/D of 84"/3.5" Extr. L/D: 24:1 # Feed Flights: 5 Feed Depth: 0.600 to 0.700 in # Metering Flights: 5 to 12 Metering Depth: 0.240 to 0.280 in Comp. Ratio: 2.0 to 2.5 Other Barrel Temperatures:Gate Temperature: 350°FAfter start-up, temperature adjustments up or down may be necessary until extrusion impact, surface, and die flow are acceptable. Adjustments in 5°F increments are recommended. Normally Zone 1 temperature should not be varied since feed rate may be affected.If a screen pack is used, a 20/40 mesh combination should be sufficient.

Category:	PVC, Rigid , Rigid Polyvinyl Chloride
Manufacturer:	Axiall Corporation
Trademark:	Axiall PVC
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0gXY54_Axiall-PVC-HHP-190.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Wellamid® GF43-66/6 XE-N	Wellman Engineering Resins	Nylon 66/6	Wellamid®
Trithene® TX 8024	Petroquimica Triunfo	LDPE	Trithene®
4MID® 9B22250 H	4Plas	Nylon 6	4MID®
Kingfa HG-542	Kingfa	PP, Unspecified	Kingfa
POLIMAXX 1126NK	IRPC Public Company Limited	PP Homopolymer	POLIMAXX