Category: | Nylon 12 , Polyamide 12 |
Manufacturer: | SABIC Innovative Plastics |
Trademark: | LNP™ LUBRICOMP™ |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 0gWtzE_LNPLUBRICOMPSFL2Acompound.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
LNP LUBRICOMP SFL2A is a compound based on Nylon 12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound SFL-402-10 Product reorder name: SFL2A |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus 1 | 16100 | MPa | ASTM D638 |
Tensile Strength (Break) | 150 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
Flexural Modulus | 13100 | MPa | ASTM D790 |
Flexural Strength | 241 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
Unnotched Izod Impact (23°C) | 910 | J/m | ASTM D4812 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 174 | °C | ASTM D648 |
Note Message | |
---|---|
1 . | 50 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
TORZEN® U4632HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
ColorFast® PCT2014 | LTL Color Compounders, Inc. | PC+PBT | ColorFast® |
EL-Lene™ H6105JU | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
Haysite Plastics HTF | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
Karina ORANGE PVC COMPOUND 750-32/34-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |