Kinta R4-006 BK
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0gHGXC_KintaR4006BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kinta R4-006 BK is a polyphenylene sulfide (PPS) product,. It is available in the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 135 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus 3 | 14500 | MPa | ASTM D790 |
| Flexural Strength 4 | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 7.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | °C | ASTM D648 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Arc Resistance | 122 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 290 - 320 | °C | |
| Mold Temperature | 110 - 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2845 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Borealis PE BB2541 | Borealis AG | HDPE | Borealis PE |
| Europrene® SOL R C2564-T | Versalis S.p.A. | SBR, Solution | Europrene® |
| PENTAMID AB E5 H schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| POCAN® B 3233 HR 000000 | LANXESS GmbH | PBT | POCAN® |