Celstran® PP-GF50-02-Black
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0epcGS_Celstran-PP-GF50-02-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% long strand glass fiber chemically coupled polypropylene, Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 11000 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 121 | MPa | ASTM D638 |
| Fracture | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.4 | % | ASTM D638 |
| Fracture | 1.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 34 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 154 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 220 - 230 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 230 to 250°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6906 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 4003 AR 10 | RTP Company | PPA | RTP |
| Sindustris PBT HI2101M | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| TOTAL Polypropylene PPH 3825WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| VAMPEEK B 0024 | Vamp Tech | PEEK | VAMPEEK |