Generic PP Homopolymer - Glass Bead
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0eAhIn_Generic-PP-Homopolymer---Glass-Bead.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass Bead This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.02 - 1.24 | g/cm³ | ASTM D792 |
| 23°C | 0.814 - 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation | |||
| Fracture, 23°C | 2.5 - 10 | % | ASTM D638 |
| Fracture, 23°C | 3.9 - 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1500 - 3510 | MPa | ASTM D790 |
| 23°C | 1550 - 1610 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 - 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 105 - 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 64.6 - 133 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 - 155 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 81.9 - 82.7 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 209 - 253 | °C | |
| Middle Temperature | 210 - 253 | °C | |
| Front Temperature | 210 - 253 | °C | |
| Mold Temperature | 48.6 - 55.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass BeadThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP2010 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| Moplen EP200S | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Wondel® A AN0F | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| Hylon® N1213L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| ULTEM™ HU2310 resin | SABIC Innovative Plastics | PEI | ULTEM™ |