Novalloy-S S4210 (TypeV)
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0e2Bll_Novalloy-S-S4210-TypeV-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-S S4210 (TypeV) is a Polycarbonate + ABS (PC+ABS) material filled with 10% glass fiber. It is available in Asia Pacific. Primary attribute of Novalloy-S S4210 (TypeV): Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 59.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4200 | MPa | ISO 178 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 116 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 106 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 26 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 70.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 4 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 100 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 150 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 267 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 150 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 200 to 240 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 20.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zetpol® 1000L | Zeon Chemicals L.P. | NBR | Zetpol® |
| Absolac® 200EP | Styrolution | ABS | Absolac® |
| ELASTOSIL® LR 3071/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| EPT K-9720 | Mitsui Chemicals, Inc. | EPDM | EPT |
| Auracell® CAP H2 | Rotuba Extruders, Inc. | CAP | Auracell® |