Vi-Chem PVC V143-90I-7081
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0dg006_Vi-Chem-PVC-V143-90I-7081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vi-Chem PVC V143-90I-7081 is a Flexible Polyvinyl Chloride material. It is available in North America for injection molding. Typical application of Vi-Chem PVC V143-90I-7081: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 89 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | > 13.0 | MPa | ASTM D638 |
| Yield | > 13.0 | MPa | ISO 527-2/2/500 |
| Tensile Elongation (Break) | > 280 | % | ASTM D638, ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 50.0 | kN/m | ASTM D624 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | -1.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air | -10 | % | ASTM D573 |
| Change in Mass in Air | 1.6 | % | ASTM D573 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility 3(-23°C) | No cracking |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability | SE | ISO 3795 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Stability 4 | 4.00 to 5.00 | ||
| Florida Weathering 5 | > 5.00 | ||
| Soiling 6 | Pass | ||
| Xenon Weatherometer 7 | > 5.00 |
| Note Message | |
|---|---|
| 1 . | Type II, 500 mm/min |
| 2 . | Die C, 50 mm/min |
| 3 . | FLTM BN 2-1 |
| 4 . | AATCC |
| 5 . | 12 months, 5° South |
| 6 . | FLTM BN 112-01 |
| 7 . | SAE J1885, 600 kJ/m², AATCC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOCOMP® A-5 TS0 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| TRIREX® 3026PJ(B1) | Samyang Corporation | PC | TRIREX® |
| NILENE® E K10T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| LNP™ LUBRICOMP™ KP004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| LEXAN™ XHT3171 resin | SABIC Innovative Plastics | PC | LEXAN™ |