Niplene F30 AGR
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niplene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0dS9gp_Niplene-F30-AGR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, reinforced with 30% glass fibre chemically coupled to the polymeric matrix |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.60 | % | |
| Across Flow | 0.40 to 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.3 | % | ASTM D638 |
| Flexural Modulus 3 | 6000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 80 | J/m | |
| 23°C, 3.20 mm | 130 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 153 | °C | ASTM D648 |
| Vicat Softening Temperature | 144 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALAC™ 310T | SAX Polymers | ABS | SAXALAC™ |
| Spartech Polycom SS1080U | Spartech Polycom | ASA | Spartech |
| Moplen HP501H | LyondellBasell Industries | PP Homopolymer | Moplen |
| OmniLon™ PA6/6 MS2 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Sylvin 4299-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |