Generic SPS - Glass Fiber
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0cysEc_Generic-SPS---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SPS - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.54 | g/cm³ | ASTM D792 |
| 23°C | 1.14 - 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.15 - 0.60 | % | ASTM D955 |
| 23°C | 0.20 - 0.66 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 9.0E-3 - 0.011 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 - 0.021 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 6670 - 12100 | MPa | ASTM D638 |
| 23°C | 7190 - 13700 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 75.0 - 130 | MPa | ISO 527-2 |
| 23°C | 84.5 - 126 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.2 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 1.3 - 2.0 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 2.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 6620 - 11900 | MPa | ASTM D790 |
| 23°C | 5000 - 13200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 103 - 188 | MPa | ASTM D790 |
| 23°C | 120 - 203 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 - 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 28 - 47 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 51 - 110 | J/m | ASTM D256 |
| 23°C | 7.9 - 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 210 - 610 | J/m | ASTM D256 |
| 23°C | 26 - 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 259 - 269 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 265 - 267 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 198 - 246 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 220 - 250 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 - 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.8E-5 - 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 109 - 130 | °C | UL 746 |
| RTI Imp | 105 - 120 | °C | UL 746 |
| RTI | 105 - 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 8.9E+15 - 1.2E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 24 - 50 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.98 - 3.22 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.0E-3 - 2.7E-3 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 135 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 270 - 302 | °C | |
| Middle Temperature | 280 - 302 | °C | |
| Front Temperature | 290 - 302 | °C | |
| Processing (Melt) Temp | 295 - 310 | °C | |
| Mold Temperature | 64.1 - 111 | °C | |
| Injection Pressure | 85.3 - 86.2 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SPS - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 4.5 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Sylvin 9700-90 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Andur 800 DP/Curene® 442 | Anderson Development Company | PUR-Est/eth,TDI | Andur |
| DENKA POVAL PC-5000F | Denka Company Limited | PVOH | DENKA POVAL |
| ULTEM™ 2212R resin | SABIC Innovative Plastics | PEI | ULTEM™ |